SWD8032 solvent free polyaspartic anticorrosion coating
Features and benefits
* high solids, low density, with good leveling, the coating film is tough, dense, full bright
* excellent adhesive strength, good compatible with polyurethane, epoxy and other material.
* high hardness, good scratch resistance and stain resistance
* excellent abrasion resistance and impact resistance
* excellent anticorrosion property, resistance to acid, alkali, salt and others.
* no yellowing, no color change, no pulverization, anti-aging, it has excellent weather resistance and light and color retention.
* can be used as a topcoat direct to metal surface (DTM)
* this product is environmentally friendly and contains no benzene solvents and lead compounds.
* can be applied in the low temperature of -10℃, the coating is dense, fast cure.
Product information
| Item | A component | B component |
| Appearance | light yellow liquid | Color adjustable |
| Specific gravity(g/m³) | 1.05 | 1.60 |
| Viscosity (cps)@25℃ | 600-1000 | 800-1500 |
| Solid content (%) | 98 | 97 |
| Mix ratio (by weight) | 1 | 2 |
| Surface dry time (h) | 0.5 | |
| Pot life h (25℃) | 0.5 | |
| Theoretical coverage (DFT) | 0.15kg/㎡ film thickness 100μm | |
Typical physical properties
| Item | Test standard | Results |
| Pencile hardness | 2H | |
| Adhesive strength (Mpa) metal base | HG/T 3831-2006 | 9.3 |
| Adhesive strength (Mpa) concrete base | HG/T 3831-2006 | 3.2 |
| Impermeability | 2.1Mpa | |
| Bending test (cylindrical axis) | ≤1mm | |
| Abrasion resistance (750g/500r) mg | HG/T 3831-2006 | 12 |
| Impact resistance kg·cm | GB/T 1732 | 50 |
| Anti-aging, accelerated aging 2000h | GB/T14522-1993 | Loss of light＜1, chalking ＜1 |
|